Fabrication of anti-aging TiO2 nanotubes on biomedical Ti alloys
Document Type
Article
Publication Date
5-2-2014
Abstract
The primary objective of this study was to fabricate a TiO2 nanotubular surface, which could maintain hydrophilicity over time (resist aging). In order to achieve non-aging hydrophilic surfaces, anodization and annealing conditions were optimized. This is the first study to show that anodization and annealing condition affect the stability of surface hydrophilicity. Our results indicate that maintenance of hydrophilicity of the obtained TiO2 nanotubes was affected by anodization voltage and annealing temperature. Annealing sharply decreased the water contact angle (WCA) of the assynthesized TiO2 nanotubular surface, which was correlated to improved hydrophilicity. TiO2 nanotubular surfaces are transformed to hydrophilic surfaces after annealing, regardless of annealing and anodization conditions; however, WCA measurements during aging demonstrate that surface hydrophilicity of non-anodized and 20 V anodized samples decreased after only 11 days of aging, while the 60 V anodized samples maintained their hydrophilicity over the same time period. The nanotubes obtained by 60 V anodization followed by 600 uC annealing maintained their hydrophilicity significantly longer than nanotubes which were obtained by 60 V anodization followed by 300°C annealing. © 2014 Hamlekhan et al.
Publication Title
PLoS ONE
Recommended Citation
Hamlekhan, A.,
Butt, A.,
Patel, S.,
Royhman, D.,
Takoudis, C.,
Sukotjo, C.,
Yuan, J.,
Jursich, G.,
Mathew, M.,
Hendrickson, W.,
Virdi, A.,
&
Shokuhfar, T.
(2014).
Fabrication of anti-aging TiO2 nanotubes on biomedical Ti alloys.
PLoS ONE,
9(5).
http://doi.org/10.1371/journal.pone.0096213
Retrieved from: https://digitalcommons.mtu.edu/michigantech-p/13378